 | | Re: Home made weight bricks and train base plates —Sonnich Jensen
|
| | | (...) I know there is tin in it, but lead - dont know. Its melting point should be a little above 100C. A friend of mine tells, that there should not be Cadmium in it, as Cadmium is toxic. (In our case they would probably end in a model rather than (...) (20 years ago, 17-Aug-04, to lugnet.parts.mod)
|
| | | |
| | | | | Re: Home made weight bricks and train base plates —David Laswell
|
| | | | (...) Lead is usually added in a very small amount to make it flow into fine detail better. It's probably only a few percent lead content, so handling it wouldn't bear anywhere near the same risk of lead poisoning that handling pure lead does. (...) (...) (20 years ago, 17-Aug-04, to lugnet.parts.mod)
|
| | | | |
| | | | | | Re: Home made weight bricks and train base plates —Mark Bellis
|
| | | | (...) Yes, always wash your hands after handling solder! (...) I see the melting point of standard solder (63% tin, 37% lead) is 183 deg C. If I held a soldering iron and a reel of solder over an invered brick and dripped molten solder into the (...) (20 years ago, 18-Aug-04, to lugnet.parts.mod)
|
| | | | |
| | | | | | Re: Home made weight bricks and train base plates —David Laswell
|
| | | | | (...) It's not just after handling it that you need to worry about. The acid in your skin will leech trace amounts from the surface, and you'll absorb it through your skin. You'd need to go out of your way to poison yourself in this manner, but you (...) (20 years ago, 18-Aug-04, to lugnet.parts.mod)
|
| | | | | |
| | | | | | Re: Home made weight bricks and train base plates —Mathew Clayson
|
| | | | (...) Unfortuneatly the drips of solder would not stick to each other, so unless you put a few drops of glue in afterwards to hold it all togather, you'd loos you weights. But this isn't a bad solution. It would fill the brick near solid, and the (...) (20 years ago, 19-Aug-04, to lugnet.parts.mod)
|
| | | | |